johnod wrote:Recently i took my exhaust off to repair a stripped stud, and discovered a missing part.
I have a Supertrap 6 into 2 stainless system, there are small nipples or spigots which slide into the end of each pipe where they bolt to the head.
I'm missing one.
Does anyone have a spare or know where i might get one?
Thanks for any help.
Those look great,what did you use on them?
I use sandpaper and lots of water on my all stainless Pipemasters. Wetsand with #1000, then #2000 and finally #3000 . . . . no polishing needed - When you're done, they look like brand new chromejohnod wrote:Those look great,what did you use on them?
barryadam wrote:Now they look like this....
Stainless Passivation See Photos of Passivating
In years gone by, the process specified was to "pickle and passivate" - a two step method - in order to create a surface on stainless steel that would be resistant to corrosion. Today, we differentiate between the two. It is two separate processes. Pickling (or Chemical Descaling) is done to remove scale. Passivation of stainless steel is done to make the surface more passive and corrosion resistant.
The passivation of stainless steel is a process performed to make a surface passive, i.e., a surface film is created that causes the surface to lose its chemical reactivity. Stainless steel passivation unipotentializes the stainless steel with the oxygen absorbed by the metal surface, creating a monomolecular oxide film. Passivation can result in the very much-desired low corrosion rate of the metal.
The passivation of stainless steel is performed when free iron, oxide scale, rust, iron particles, metal chips or other nonvolatile deposits might adversely affect the metallurgical or sanitary condition or stability of the surface, the mechanical operation of a part, component or system, or contaminate the process fluid.
Passivation is performed on clean stainless steel, providing the surface has been thoroughly cleaned or descaled. Since the term "passivation" is used to describe distinctly different operations or processes relating to stainless steels, it is necessary to define precisely what is meant by passivation.
What is Stainless Steel Passivation?
Stainless passivation is the process by which stainless steel will spontaneously form a chemically inactive surface when exposed to air or other oxygen-containing environments. Some important facts to know when considering stainless steel passivation:
* Steels containing more than 11% Chromium are capable of forming an invisible, inert or passive, self-repairing oxide film on their surface. It is this passive layer that gives stainless steels their corrosion resistance.
* If a stainless steel surface is scratched, then more Chromium is exposed which reacts with oxygen allowing the passive layer to reform. However, if a particle of carbon steel is embedded in the scratch then the passive layer cannot reform and corrosion will occur when the metal is wetted or exposed to a corrosive environment.
* Stainless passivation is the chemical treatment of a stainless steel surface with a mild oxidant such as citric acid passivation solution. This process is to accelerate the process noted above in No. 1.
* Passivation is the removal of exogenous iron or iron compounds from the surface of stainless steel by means of a chemical dissolution, most typically by a treatment with an citric acid passivation solution that will remove the surface contamination but will not significantly affect the stainless steel itself.
* Passivation also is accomplished by electropolishing. Electropolishing is an electrochemical process that is a super passivator of stainless steel and results in a more passive surface than the other methods mentioned above.
This last step is necessary because during handling and processing such as rolling, forming, machining, pressing, tumbling, and lapping, particles of iron or tool steel or abrasive particles may be embedded in or smeared on or into the surfaces of stainless steel components. If allowed to remain, these particles may corrode and produce rust spots on the stainless steel. This is due to the formation of a galvanic couple between two dissimilar metals that can promote a corrosive reaction. To dissolve the embedded or smeared iron and prevent this condition, as well as restore the original corrosion-resistant surface, semi-finished or finished parts are given a 'passivation' treatment.